PC/PBT-H10 Brief Description
Grade Name：PC/PBT-H10
|
Material Type |
PC/PBT alloy |
Features |
Gas assisted, high-intensity |
|
Process Method |
injection molding |
Applications |
Car exterior handle |
General Properties
|
Properties |
Unit |
Test Method |
Test Condition |
Typical Values |
|
Physical Property |
||||
|
Density |
g/cm³ |
GB/T 1033 |
23℃ |
1.15 |
|
Melt Mass-Flow Rate |
g/10min |
GB/T 3682 |
250℃,5kg |
32 |
|
Mechanical Property |
||||
|
Tensile Strength |
MPa |
GB/T 1040 |
50mm/min |
48 |
|
Tensile Elongation at Break |
％ |
GB/T 1040 |
50mm/min |
47 |
|
Flexural Strength |
MPa |
GB/T 9341 |
2mm/min |
70 |
|
Flexural Modulus |
MPa |
GB/T 9341 |
2mm/min |
2100 |
|
Izod Impact Strength |
kJ/m² |
GB/T 1843 |
5.5J |
NB |
|
Notched Izod Impact Strength |
kJ/m² |
GB/T 1843 |
2.75J |
53 |
|
热性能 Thermal Property |
||||
|
HDT |
℃ |
GB/T 1634 |
0.45MPa |
95 |
Note:
1. Testing environment: temperature of 23 ℃, relative humidity of 50RH%.
2. The data in the above table are typical values in experiments and production, and are only for reference during use, not as product standards.